Študija mikrostrukture in mehanskih lastnosti lasersko varjenega spoja iz titanove zlitine 1,5 mm Ti-6Al-4V

ključne besede:Ti-6Al-4V titanova zlitina/ lasersko varjenje / mikrostruktura / mehanske lastnosti

Avtorji: Fu Heguo, Liu Guangxin, Xie Hongzhi, Jiang Wentong itd.

Shenyang Aircraft Industry Group Co., Ltd

Vir: varjenje in rezanje

Povzetek: poskus laserskega varjenja plus varjenje z modifikacijo površine 1,5 mmTi-6Al-4V titanova zlitina was carried out, and the microstructure and static properties of the joint were observed. The results show that due to the influence of different welding thermal cycles, The structure area of laser welding plus surface modification welding joint can be divided into a base metal area, heat affected area, equiaxed crystal area at the bottom of weld, and columnar crystal area at the top of the weld, there is widmanstatten structure in the weld structure, With the increase of the distance from the fusion line, the microstructure of the heat-affected zone increases ' The volume fraction decreased gradually.

Mehanske lastnosti spoja kažejo, da sta natezna trdnost in strižna trdnost enakovredni osnovni kovini, najmanjši upogibni kot pa je 35 stopinj, kar kaže, da je spoj mogoče uporabiti v inženirstvu.

Morfologija zvarnega spoja iz titanove zlitine Ti-6Al-4V

Mikrostruktura zvarnega območja

Morfologija mikrostrukture različnih regij v toplotno prizadetem območju

Preskusna vrednost mehanskih lastnosti spoja

Povprečna vrednost mehanskih lastnosti spoja